Avoiding rod breakage.
We often see rods for repair with damage that could have been avoided. We hope this information will help with understanding the structure and behaviour of your rods so that you will be able to make sure you are not back in the shop asking for a repair instead of fishing!
A little understanding of how pressure is distributed throughout a rod blank will result in a lower chance of breakages due to accidental mishandling.
The natural curve of a rod is when the full length of the rod is used in a casting or playing action (as indicated). In this situation the rod is very strong, because as the pressure increases, the forces travel down the blank towards the larger diameter of the butt, which is designed to deal with this build-up of pressure. However, if the natural curve is interfered with or restricted in some way, accidental breakages can occur.
Rolling process defects
These are usually twisting of the carbon fibres or a foreign object gets rolled into the blank during the rolling process. On close inspection of the break irregular folds or the object will be seen.
IMPACT OR PRESSURE POINT DAMAGE
These are the cause of many seemingly unexplainable breakages. An invisible fracture can occur if a rod receives a short sharp impact or is put under pressure during storage or transportation. The weak point created may then cause a breakage the next time the rod is used.
Many impact fractures show tell-tail marks around the break, but pressure point fractures can leave no evidence of the cause. Most carp rods are very durable and can withstand heavy handling, but care should always be taken to make sure they are handled, transported and stored in a way that prevents these problems.